|本期目录/Table of Contents|

[1]杨晓隆,黄建花. 溶液pH值对PbWO4晶相和形貌的影响[J].浙江理工大学学报,2012,29(05):734-739.
 YANG Xiao long,HUANG Jian hua. Control of PbWO4 Crystal Phase and Morphologyunder Varying pH Conditions[J].Journal of Zhejiang Sci-Tech University,2012,29(05):734-739.
点击复制

 溶液pH值对PbWO4晶相和形貌的影响()
分享到:

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第29卷
期数:
2012年05期
页码:
734-739
栏目:
(自科)生物与生命科学
出版日期:
2012-10-28

文章信息/Info

Title:
 Control of PbWO4 Crystal Phase and Morphologyunder Varying pH Conditions
文章编号:
16733851 (2012) 05073406
作者:
 杨晓隆 黄建花
 浙江理工大学化学系, 杭州 310018
Author(s):
 YANG Xiaolong HUANG Jianhua
 Department of Chemistry, Zhejiang SciTech University, Hangzhou 310018, China
关键词:
 钨酸铅 pH 晶体生长 荧光
分类号:
O78
文献标志码:
A
摘要:
    在30℃下,以Na2WO4和Pb(NO3)2为原料,通过沉淀反应制备PbWO4晶体。考察Pb(NO3)2溶液的pH值对PbWO4的晶型和形貌的影响。通过XRD、Raman和SEM等表征,发现在酸性和碱性溶液中分别得到了梭状和八面体状的四方晶相PbWO4晶体,而在中性溶液中,得到单斜晶相PbWO4纳米带,表明pH值显著影响PbWO4的晶型和形貌。室温下,以300 nm为激发波长研究产物的固体荧光光谱,发现碱性条件下得到的四方相PbWO4八面体具有最强的绿发光带,表明PbWO4的荧光性质受其晶型和形貌影响。

参考文献/References:

 [1]Gratta G, Newman H, Zhu R Y. Crystal calorimeters in particle physics[J]. Annu Rev Nucl Part Sci, 1994, 44(1): 453500.
[2] Nikl M, Bohacek P, Mihokova E, et al. Enhanced efficiency of PbWO4: Mo, Nb scintillator[J]. J Appl Phys, 2002, 91(8): 50415044.
[3] Kobayashi M, Ishii M, Usuki Y, et al. Scintillation characteristics of PbWO4 singlecrystals at roomtemperature[J]. Nucl Instrum Meth A, 1993, 333(2/3): 429433.
[4] Geng J, Zhu J J, Lu D J, et al. Hollow PbWO4 nanospindles via a facile sonochemical route[J]. Inorg Chem, 2006, 45(20): 84038407.
[5] Zhang Q, Yao W T, Chen X Y, et al. Nearly monodisperse tungstate MWO4 microspheres (M=Pb, Ca): surfactantassisted solution synthesis and optical properties[J]. Cryst Growth Des, 2007, 7(8): 14231431.
[6] Wang G Z, Hao C H. Fast synthesis and morphology control of lead tungstate microcrystals via a microwaveassisted method[J]. Mater Res Bull, 2009, 44(2): 418421.
[7] Thongtem T, Kaowphong S, Thongtem S. Sonochemical preparation of PbWO4 crystals with different morphologies[J]. Ceram Int, 2009, 35(3): 11031108.
[8] Chen D, Shen G Z, Tang K B, et al. AOTmicroemulsionsbased formation and evolution of PbWO4 crystals[J]. J Phys Chem B, 2004, 108(31): 1128011284.
[9] Zhou G J, Lu M K, Gu F, et al. Morphologycontrolled synthesis, characterization and growth mechanism of PbWO4 nano and macrocrystals[J]. J Cryst Growth, 2005, 276(3/4): 577582.
[10] Wu N C, Shi E W, Zheng Y Q, et al. Effect of pH value of medium on hydrothermal synthesis of nanocrystalline zirconia powders[J]. China Powder Sci Technol, 2000, 6(S): 284286.
[11] Yang J H, Lu C H, Su H, et al. Morphological and structural modulation of PbWO4 crystals directed by dextrans[J]. Nanotechnology, 2008, 19(3): 035608035614.
[12] Zheng C H, Hu C G, Chen X Y, et al. Raspite PbWO4 nanobelts: synthesis and properties[J]. Cryst Eng Comm, 2010, 12(10): 32773282.
[13] George T, Joseph S, Sunny A T, et al. Fascinating morphologies of lead tungstate nanostructures by chimie douce approach[J]. J Nanopart Res, 2008, 10(4): 567571.
[14] Luke L Y Chang. Phase relations in the system PbOWO3[J]. J Am Ceram Soc, 1971, 54(7): 357358.
[15] Bastians S, Crump G, Griffith W, et al. Raspite and studtite: raman spectra of two unique minerals[J]. J Raman Spectrosc, 2004, 35(8/9): 726731.
[16] Ishii M, Harada K, Kobayashi M, et al. Mechanical properties of PbWO4 scintillating crystals[J]. Nucl Instr Meth Phys Res A, 1996, 376(2): 203207.
[17] Errandonea D, PellicerPorres J, Manjón F J, et al. Determination of the highpressure crystal structure of BaWO4 and PbWO4[J]. Phys Rev B, 2006, 73(22): 224103224117.
[18] Yu S H, Liu B, Mo M S, et al. General synthesis of singlecrystal tungstate nanorods/nanowires: a facile, lowtemperature solution approach[J]. Adv Funct Mater, 2003, 13(8): 639647.
[19] Liu B, Yu S H, Li L J, et al. Morphology control of stolzite microcrystals with high hierarchy in solution[J]. Angew Chem Int Ed, 2004, 43(36): 47454750.
[20] Chen D, Tang K B, Li F Q, et al. A simple aqueous mineralization process to synthesize tetragonal molybdate microcrystallites[J]. Cryst Growth Design, 2006, 6(1): 247252.
[21] Jun Y W, Lee J H, Choi J S, et al. Symmetrycontrolled colloidal nanocrystals: nonhydrolytic chemical synthesis and shape determining parameters[J]. J Phys Chem B, 2005, 109(31): 1479514806.
[22] Liu B, Yu S H, Li L J, et al. Morphology control of stolzite microcrystals with high hierarchy in solution[J]. Angew Chem Int Ed, 2004, 43(36): 47454750.
[23] Geng J, Zhu J, Chen H. Sonochemical preparation of luminescent PbWO4 nanocrystals with morphology evolution[J]. Cryst Growth Des, 2006, 6(1): 321326.
[24] Geng J, Lu Y, Lu D, et al. Sonochemical synthesis of PbWO4 crystals with dendritic, flowery and starlike structures[J]. Nanotechnology, 2006, 17(10): 26142620.
[25] Babin V, Bohacek P, Krasnikov A, et al. Origin of green luminescence in PbWO4 crystals[J]. J Lumin, 2007, 124(1): 113119.
[26] Van Loo W. Luminescence of lead molybdate and lead tungstate[J]. Phys Status Solidi (a), 1975, 27(2): 565574.
[27] Lei F, Yan B, Chen H H, et al. Surfactantassisted hydrothermal synthesis, physical characterization and photoluminescence of PbWO4[J]. Cryst Growth Des, 2009, 9(9): 37303736.
[28] Blasse G. Classical phosphors: a pandoras box[J]. J Lumin, 1997, 7274: 129134.
[29] Nikl M. Wide band gap scintillation materials: progress in the technology and material understanding[J]. Phys Status Solidi (a), 2000, 178(2): 595620.

相似文献/References:

[1]陈智杰a,赵晓丽a,徐畅b,等. 有机颜料微胶囊在涂料染色中的应用及其染色效果分析[J].浙江理工大学学报,2013,30(01):1.
 CHEN Zhi jiea,ZHAO Xiao lia,XU Changb,et al. Application of Organic Pigment Microcapsule in Pigment Dyeingand Its Dyeing Results[J].Journal of Zhejiang Sci-Tech University,2013,30(05):1.
[2]詹永娟,谢维斌,姜晓云,等. 织物液态水传递性能的自动检测技术及应用[J].浙江理工大学学报,2013,30(01):6.
 ZHAN Yong juan,XIE Wei bin,JIANG Xiao yun,et al. Technology and Application of the Automatic Detection inTesting Liquid Transport Properties of Textiles[J].Journal of Zhejiang Sci-Tech University,2013,30(05):6.
[3]孙麒. 基于极大似然估计的织物图像分割[J].浙江理工大学学报,2013,30(01):12.
 SUN Qi. Textile Image Segmentation Based on theMaximum Likelihood Algorithm[J].Journal of Zhejiang Sci-Tech University,2013,30(05):12.
[4]巫静a,田彦杰b,汪澜a,等. 基于SVM理论的涤纶织物分散染料上染率模型研究[J].浙江理工大学学报,2013,30(01):21.
 WU Jinga,TIAN Yan jieb,WANG Lana,et al. Research on Modeling of DyeUptake Rate for Disperse Dyes onPolyester Fibers Based on SVM[J].Journal of Zhejiang Sci-Tech University,2013,30(05):21.
[5]周昊,徐英莲,齐素梅.微孔结构改性涤纶/棉混纺针织物服用性能的研究[J].浙江理工大学学报,2013,30(01):21.
 ZHAO Hao,XU Ying lian,QI Su mei. Research on Using Knitted Blend Fabric of Modified Polyesterby Cellular Structure and Cotton for Wearing[J].Journal of Zhejiang Sci-Tech University,2013,30(05):21.
[6]孙佳英,李艳清,章斐燕,等. 纺织结构复合材料铺层顺序设计与力学性能分析[J].浙江理工大学学报,2013,30(01):27.
 SUN Jia ying,LI Yan qing,ZHANG Fei yan,et al. Study on Layer Sequence Design and Mechanical Propertiesof Textile Structure Composites[J].Journal of Zhejiang Sci-Tech University,2013,30(05):27.
[7]丁源维,王騊,姚菊明,等. 静电纺制备TiO2/PVA复合纳米纤维及其光催化性能研究[J].浙江理工大学学报,2013,30(01):31.
 DING Yuan wei,WANG Tao,YAO Ju ming,et al. Photocatalytic Performance Investigation of TiO2/PVANanofibers Prepared by Electrospinning[J].Journal of Zhejiang Sci-Tech University,2013,30(05):31.
[8]章梦洁,伍仲,方园. 涤棉混纺织物阻燃性能的实验分析[J].浙江理工大学学报,2013,30(01):36.
 ZHANG Meng jie,WU Zhong,FANG Yang. Experimental Study on the PolyesterCotton BlendedFabrics Flame Retardancy[J].Journal of Zhejiang Sci-Tech University,2013,30(05):36.
[9]胡觉亮a,孔云鹏b,韩曙光a,等. 基于随机需求的服装供应链回购契约研究[J].浙江理工大学学报,2013,30(01):40.
 HU Jue lianga,KONG Yun pengb,HAN Shu guanga,et al. Study on Repurchase Contract in a Fashion Chainwith the Stochastic Demand[J].Journal of Zhejiang Sci-Tech University,2013,30(05):40.
[10]毛雯,阎玉秀. 针织服装供应商评价指标体系构建与权重确定[J].浙江理工大学学报,2013,30(01):46.
 MAO Wen,YAN Yu xiu. Building Evaluation Index System for Knitting Clothing Suppliersand Determining the Weight[J].Journal of Zhejiang Sci-Tech University,2013,30(05):46.

备注/Memo

备注/Memo:
 收稿日期: 2012-04-28
基金项目: 浙江理工大学研究生创新基金项目(YCXS1101)
作者简介: 杨晓隆(1987-),男,安徽界首人,硕士研究生,研究方向为材料仿生合成。
通讯作者: 黄建花,电子邮箱:jhhuang@zstu.edu.cn
更新日期/Last Update: